321 Shirit prej çeliku inox
Furnizim Baogu i klasës së fletëve prej çeliku inox
| Lloji | Gradë | Gradë | Përbërësi kimik % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Të tjera | |||
| Austenitike | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | ≤1.00 | - | ≤0,25 | - | ||
| 301 | 1.431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - | |
| 304 | 1.4301 | ≤0.07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304 litra | 1,4307 | ≤0.030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0.08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0.08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1,4401 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316 litra | 1,4404 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316 Ti | 1,4571 | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0.08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317 litra | 1,4438 | ≤0.03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1,4541 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1.455 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| 347H | 1.494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| xm-19 | Nitronik50 | ≤0.06 | 20.50-23.50 | 11.50-13.50 | 4,0-6,0 | ≤0.045 | ≤0.030 | 1.50-3.00 | ≤1.00 | - | 0,2-0,4 | Nb: 0,10-0,30 V: 0,10-0,30 | |
| 904 litra | N08904 | ≤0.02 | 19.0-23.0 | 23.0-28.0 | 4,0-5,0 | ≤0.045 | ≤0.035 | ≤1.00 | 0.1 | Cu: 1,0-2,0 | |||
| Dupleks | 2205 | S32205 | ≤0.03 | 22.0-23.0 | 4,5-6,5 | ≤2.00 | ≤0.030 | ≤0.020 | 3,0-3,5 | ≤1.00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0.03 | 24.0-26.0 | 6,0-8,0 | ≤1,20 | ≤0.035 | ≤0.020 | 3,0-5,0 | ≤0,80 | 0.5 | 0,24-0,32 | ||
| * | S32760 | ≤0.03 | 24.0-26.0 | 6,0-8,0 | ≤1.00 | ≤0.030 | ≤0.010 | 3,0-4,0 | ≤1.00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0.03 | 21.5-24.5 | 3,0-5,5 | ≤2,50 | ≤0.040 | ≤0.030 | 0,05-0,6 | ≤1.00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1.446 | ≤0.08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0.040 | ≤0.030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Ferrit | 409 | S40900 | ≤0.03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0.040 | ≤0.020 | - | ≤1.00 | - | ≤0.030 | Ti6(C+N)~0.50 Nb:0.17 |
| 430 | 1Cr17 | ≤0.12 | 16.00-18.00 | - | ≤1.0 | ≤0.040 | ≤0.030 | - | ≤1.0 | - | - | - | |
| 444 | S44400 | ≤0.025 | 17.50-19.50 | 1 | ≤1.00 | ≤0.040 | ≤0.030 | 1,75-2,5 | ≤1.00 | - | 0,035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0.75 | ≤1.5 | ≤0.040 | ≤0.030 | 1.50-2.50 | ≤1.00 | - | ≤0,25 | - | |
| Martensit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0.75 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0.080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1,25 | ≤0.060 | ≥0.15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0.15 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1.50-2.50 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | 0.75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4 PH | ≤0.07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7 PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5 PH | ≤0,09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | ≤1.00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Përshkrim
Rrip çeliku inox 321 është një lloj çeliku inox austenit me përmbajtje të ulët karboni dhe rezistencë të mirë ndaj korrozionit në shumë mjedise gërryese.321 ofron saldueshmëri të shkëlqyer, përpunueshmëri të mirë dhe veti fabrikuese të jashtëzakonshme.
Shiriti inox 321 përdoret zakonisht në industrinë kimike, industrinë e pulpës dhe letrës, industrinë e inxhinierisë detare dhe në det të hapur, si dhe në industrinë e ushqimit dhe pijeve.
Shiriti prej çeliku inox 321 ka gjithashtu një nivel të lartë rezistence ndaj gërryerjes së stresit të klorurit dhe plasaritjes.Është gjithashtu rezistent ndaj acidit klorhidrik në temperatura të ngritura deri në 250°C (480°F).
Veçoritë
Rezistencë e mirë ndaj korrozionit: Shiriti prej çeliku inox 321 ka rezistencë më të mirë ndaj korrozionit se 304 dhe 316 lloje çeliku inox, gjë që e bën atë ideal për përdorim në mjedise korrozive.
Saldueshmëri e shkëlqyeshme: Rrip çeliku inox 321 mund të saldohet me të gjitha metodat, duke përfshirë saldimin me hark (TIG / GTAW), saldimin me rreze elektronike (EBW / EFW), saldimin me hark të zhytur (SAW) dhe saldimin me rreze lazer (LBIW).
Fortësi e lartë: Nivelet e forcës së shiritit inox 321 janë deri në 50% më të larta se ato të 304 llojeve të çeliqeve inox dhe deri në 80% më të larta se ato të 316 llojeve të çeliqeve inox për shkak të rritjes së përmbajtjes së tyre të karbonit dhe madhësisë së kokrrizave të austenitit.